Suppose that a wing component on an aircraft is fabricated from an aluminum alloy that has a plane-strain fracture toughness of 26.0 MPa m0.5. It has been determined that fracture results at a stress of 112 MPa when the maximum internal crack length is 8.6 mm. For this same component and alloy, compute the stress level at which fracture will occur for a critical internal crack length of 3.0 mm.

the required stress level  at which fracture will occur for a critical internal crack length of 3.0 mm is 189.66 MPa

Explanation:

From the given information; the objective is to compute the stress level at which fracture will occur for a critical internal crack length of 3.0 mm.

The Critical Stress for a maximum internal crack can be expressed by the formula:

where;

= critical stress required for initiating crack propagation

= plain stress fracture toughness = 26 Mpa

Y = dimensionless parameter

a = length of the internal crack

given that ;

the maximum internal crack length is 8.6 mm

half length of the internal  crack will be 8.6 mm/2 = 4.3mm

half length of the internal  crack a = 4.3 × 10⁻³ m

From :

For this same component and alloy, we are to also compute the stress level at which fracture will occur for a critical internal crack length of 3.0 mm.

when the length of the internal crack a = 3mm

half  length of the internal  crack will be 3.0 mm / 2 = 1.5 mm

half length of the internal  crack a =1.5 × 10⁻³ m

From;

189.66 MPa

Thus; the required stress level  at which fracture will occur for a critical internal crack length of 3.0 mm is 189.66 MPa