The fatigue data for a ductile cast iron are given as follows: stress amplitude [mpa (ksi)] cycles to failure 248 (36.0) 1 × 105 236 (34.2) 3 × 105 224 (32.5) 1 × 106 213 (30.9) 3 × 106 201 (29.1) 1 × 107 193 (28.0) 3 × 107 193 (28.0) 1 × 108 193 (28.0) 3 × 108

(a) make an s–n plot (stress amplitude versus logarithm cycles to failure) using these data.

(b) what is the fatigue limit for this alloy?

(c) determine fatigue lifetimes at stress amplitudes of 230 mpa (33,500 psi) and 175 mpa (25,000 psi).

(d) estimate fatigue strengths at 2 × 105 and 6 × 106 cycles.

Answers: 1

Show answers

Another question on Engineering

Engineering, 04.07.2019 18:10

The higher the astm grain-size number, the coarser the grain is. a)-true b)-false

Answers: 3

Answer

Engineering, 04.07.2019 18:10

Which of the following ziegler nichols tuning methods the response of the controller to a step input should exhibit an s-shaped curve? a)-open loop mode b)-closed loop mode c)-both modes (open & closed) d)-none of the modes (open & closed)

Answers: 3

Answer

Engineering, 04.07.2019 18:10

Ahot wire operates at a temperature of 200°c while the air temperature is 20°c. the hot wire element is a tungsten wire of 5 um diameter and 2 mm in length. plot using excel current, heat transfer and heat generated by the wire for air velocity varying from 1-10 m/s in steps of lm/s? matlab the sensor voltage output, resistance, or assume nu 0.989 re033pr13 take air properties at tr (200°c20°c)/2 = 110°c properties of tungsten: c 0.13 kj/kg.k 3 p 19250 kg/m k (thermal conductivity) = 174 w/m.k

Answers: 2

Answer

Engineering, 04.07.2019 19:10

Tom is having a problem with his washing machine. he notices that the machine vibrates violently at a frequency of 1500 rpm due to an unknown rotating unbalance. the machine is mounted on 4 springs each having a stiffness of 10 kn/m. tom wishes to add an undamped vibration absorber attached by a spring under the machine the machine working frequency ranges between 800 rpm to 2000 rpm and its total mass while loaded is assumed to be 80 kg a) what should be the mass of the absorber added to the machine so that the natural frequency falls outside the working range? b) after a first trial of an absorber using a mass of 35 kg, the amplitude of the oscillation was found to be 10 cm. what is the value of the rotating unbalance? c) using me-3.5 kg.m, find the optimal absorber (by minimizing its mass). what would be the amplitude of the oscillation of the absorber?

Answers: 3

Answer

You know the right answer?

The fatigue data for a ductile cast iron are given as follows: stress amplitude [mpa (ksi)] cycles...

Questions