An iron-carbon alloy initially containing 0.286 wt% c is exposed to an oxygen-rich and virtually carbon-free atmosphere at 1200°c. under these circumstances the carbon diffuses from the alloy and reacts at the surface with the oxygen in the atmosphere; that is, the carbon concentration at the surface position is maintained essentially at 0.0 wt% c. at what position will the carbon concentration be 0.215 wt% after a 7 h treatment? the value of d at 1200°c is 7.5 × 10-11 m2/s.

z erf(z) z erf(z) z erf(z)
0.00 0. 0.55 0.5633 1.3 0.9340
0.025 0.0282 0.60 0.6039 1.4 0.9523
0.05 0.0564 0.65 0.6420 1.5 0.9661
0.10 0.1125 0.70 0.6778 1.6 0.9763
0.15 0.1680 0.75 0.7112 1.7 0.9838
0.20 0.2227 0.80 0.7421 1.8 0.9891
0.25 0.2763 0.85 0.7707 1.9 0.9928
0.30 0.3286 0.90 0.7970 2.0 0.9953
0.35 0.3794 0.95 0.8209 2.2 0.9981
0.40 0.4284 1.0 0.8427 2.4 0.9993